 产品详细介绍 |
|
项 目
\ 牌 号 |
NZ-82 |
TP |
N2 |
CN-45 |
ASC-T |
ASC-Z |
ASC-D |
ASC-SD-T |
ASC-SD-Z |
ASC-SD-D |
ASC-H |
ASC-L |
| Al2O3 % |
≥40
|
≥42
|
|
≥45 |
≥53 |
≥53 |
≥53 |
≥57 |
≥55 |
≥62 |
≥58 |
≥60 |
| Fe2O3 % |
≤2.0 |
≤1.6
|
|
≤1.7 |
|
|
|
|
|
|
|
|
| SiC % |
|
|
|
|
≥7 |
≥5 |
≥11.5 |
|
|
|
≥10 |
≥10 |
| C % |
|
|
|
|
≥10 |
≥11.5 |
≥5 |
≥6 |
≥8 |
≥4 |
≥8 |
≥8 |
| SiC+ C % |
|
|
|
|
|
|
|
≥14 |
≥17 |
≥10 |
|
|
| Al2O3+ SiC % |
|
|
|
|
≥65 |
≥65 |
≥65 |
|
|
|
|
|
耐火度 ℃
|
≥1730
|
≥1750
|
|
|
|
|
|
|
|
|
|
|
显气孔率 %
|
≤15
|
≤15 |
≤24 |
≤17 |
≤8.5 |
≤8.5 |
≤10 |
≤10 |
≤8 |
≤10 |
≤10 |
≤8 |
体积密度 g/cm3
|
≥2.30
|
|
|
|
≥2.75 |
≥2.75 |
≥2.75 |
≥2.75 |
≥2.75 |
≥2.75 |
≥2.75 |
≥2.85 |
常温耐压强度 Mpa
|
≥49.0 |
≥58.8 |
≥24.5 |
≥40 |
≥40 |
≥40 |
≥40 |
≥40 |
≥35 |
≥45 |
≥50 |
≥50 |
| 常温抗折强度 MPa |
|
|
|
|
|
|
|
|
|
|
≥15 |
≥15 |
| 高温抗折强度 Mpa |
|
|
|
|
|
|
|
1400℃
×0.5h
≥5.5 |
1400℃
×0.5h
≥5 |
1400℃
×0.5h
≥6 |
1450℃
保护≥5 |
1450℃
保护≥8 |
| 荷重软化温度 ℃ |
T2≥1500 |
KD≥1450 |
|
|
|
|
|
|
|
|
|
|
| 重烧线变化率 % |
|
1450 ℃×3h
0～-0.2 |
1400 ℃×2h
+0.1～-0.5 |
1450 ℃×3h
+0.1～-0.3 |
|
|
|
|
|
|
1450 ℃×2h
0～0.5 |
1400 ℃×2h
0～0.7 |
| 热震稳定性,次(1100℃ 水冷) |
≥10
无剥落 |
|
|
|
|
|
|
|
|
|
|
|
| 使用部位 |
工作层
永久层 |
混铁车
工作层
|
混铁车
永久层
|
铁水罐
工作层 |
混铁车
铁水部 |
混铁车
渣线部 |
混铁车
顶部 |
混铁车
铁水部 |
混铁车
渣线部 |
混铁车
顶部
|
混铁车
直筒部 |
混铁车
锥体段 | | | |
|